\n","summary":"","keywords":"","linkUrl":"","imgUrl":"","createDate":"2024-04-17 14:17:16","type":1,"showFlag":true,"newOpen":false,"showStyle":"","detailStyle":"","showOrder":1,"hasInfoCount":19,"mobileDes":"\n","mobileLinkUrl":"","mobileNewOpen":false,"mobileShowStyle":"","mobileDetailStyle":"","mobileShowFlag":false},{"id":4,"appId":3,"useViewType":false,"parentId":6,"name":"圖片新聞","des":"

\r\n\t圖片分類

\r\n
","summary":"","keywords":"","linkUrl":"","imgUrl":"","createDate":"2024-04-22 13:31:05","type":1,"showFlag":true,"newOpen":false,"showStyle":"","detailStyle":"","showOrder":2,"hasInfoCount":17,"mobileDes":"","mobileLinkUrl":"","mobileNewOpen":false,"mobileShowStyle":"","mobileDetailStyle":"","mobileShowFlag":true}],"hasInfoCount":36,"mobileDes":"","mobileLinkUrl":"","mobileNewOpen":true,"mobileShowStyle":"","mobileDetailStyle":"","mobileShowFlag":true},{"id":5,"appId":3,"useViewType":false,"name":"渣漿泵技術支持","des":"

渣漿泵技術支持

\n","summary":"","keywords":"","linkUrl":"","imgUrl":"","createDate":"2024-04-07 08:58:26","type":1,"showFlag":true,"newOpen":true,"showStyle":"","detailStyle":"","showOrder":2,"hasInfoCount":135,"mobileDes":"","mobileLinkUrl":"","mobileNewOpen":true,"mobileShowStyle":"","mobileDetailStyle":"","mobileShowFlag":true}],"id":5,"value":"info"},{"isdef":false,"name":"companyfile","categoryList":[],"id":6,"value":"companyfile"}], id : "portalResSearch_total-15822549298004690", lib : [ "js/portalSearch/portalResSearch_total-02"], totalSite:"全站", product:"商品", info:"資訊", companyfile:"下載", recruit:"招聘", productMachine:"機械", productParts:"配件", course:"課程", teacher:"教師", atlas:"企業圖冊" });
1

1

渣漿泵技術支持

/
/
護套裂紋失效簡介-渣漿泵護套産生裂紋的原因及對策(二)

護套裂紋失效簡介-渣漿泵護套産生裂紋的原因及對策(二)

【概要描述】由達爾泵業有限公司生産的的100DZM-A39型渣漿泵安裝於山西某鋁廠氧化鋁二車間的出料泵位,運行時,泵發生漏料,打開泵後發現護套出現一道寬1~2mm的裂紋。於是,便將該護套砸開,進行了各種觀察分析,在不同部位出現了以下情形:(1)明顯漏料的裂紋斷口上(圖1a),由與護闆配合處(A處)至與填料箱配合處(B處)為光亮斷口,而由填料箱配合處至與葉輪軸配合處(C處)為已被氧化腐蝕的黑色斷口。(2)與葉輪後蓋闆相鄰的過流麵上,出現由中心孔嚮外呈放射型微觀裂紋(圖1),在放射型裂紋處砸開其斷麵後,為局部被氧化腐蝕的黑色斷口,見圖1(b)。(3)護套後側闆的斷麵上(圖1c),內側麵(過流麵)與外側麵(副葉輪室)的斷口形態分別為晶粒細小、平整、光亮和晶粒稍粗、凹凸不平、

護套裂紋失效簡介-渣漿泵護套産生裂紋的原因及對策(二)

【概要描述】由達爾泵業有限公司生産的的100DZM-A39型渣漿泵安裝於山西某鋁廠氧化鋁二車間的出料泵位,運行時,泵發生漏料,打開泵後發現護套出現一道寬1~2mm的裂紋。於是,便將該護套砸開,進行了各種觀察分析,在不同部位出現了以下情形:(1)明顯漏料的裂紋斷口上(圖1a),由與護闆配合處(A處)至與填料箱配合處(B處)為光亮斷口,而由填料箱配合處至與葉輪軸配合處(C處)為已被氧化腐蝕的黑色斷口。(2)與葉輪後蓋闆相鄰的過流麵上,出現由中心孔嚮外呈放射型微觀裂紋(圖1),在放射型裂紋處砸開其斷麵後,為局部被氧化腐蝕的黑色斷口,見圖1(b)。(3)護套後側闆的斷麵上(圖1c),內側麵(過流麵)與外側麵(副葉輪室)的斷口形態分別為晶粒細小、平整、光亮和晶粒稍粗、凹凸不平、

詳情

由達爾泵業有限公司生産的的100DZM-A39型渣漿泵安裝於山西某鋁廠氧化鋁二車間的出料泵位,運行時,泵發生漏料,打開泵後發現護套出現一道寬1~ 2mm的裂紋。於是,便將該護套砸開,進行了各種觀察分析,在不同部位出現了以下情形:

(1) 明顯漏料的裂紋斷口上 ( 圖 1a ) ,由與護 闆配合處 (A  處) 至與填料箱配合處 (B 處) 為光 亮斷口,而由填料箱配合處至與葉輪軸配合處 (C 處) 為已被氧化腐蝕的黑色斷口。

(2) 與葉輪後蓋闆相鄰的過流麵上,出現由 中心孔嚮外呈放射型微觀裂紋 ( 圖 1) ,在放射型 裂紋處砸開其斷麵後,為局部被氧化腐蝕的黑色斷口,見圖 1 (b )。

(3) 護套後側闆的斷麵上 ( 圖 1c ) ,內側麵( 過流麵) 與外側麵 ( 副葉輪室) 的斷口形態分別 為晶粒細小、平整、光亮和晶粒稍粗、凹凸不平、光亮。

 

darpump

聯係方式

 

地址:河北省石家莊市

欒城區裝備製造基地裕太路11號

源泰控股

關註官方公衆號

産品中心

渣漿泵

脫硫泵
液下渣漿泵
潛水渣漿泵
泥漿泵_抽沙泵

砂礫泵

單殼泵

襯膠渣漿泵

耐腐蝕泵

渣漿泵配件

聯係方式

 

地址:河北省石家莊市欒城區裝備製造基地裕太路11號

源泰控股

關註官方公衆號

网站地图 | xml网站地图